Type | Style | Tissage | Poids (g/m²) | Épaisseur (mm) | Largeur (m) |
---|---|---|---|---|---|
ZC-1K Plain Weave | 1K | Tissu uni | 120 | 0.16 | 0-2.3 |
ZC-1K Twill Weave | 1K | Tissu sergé | 120 | 0.16 | 0-2.3 |
ZC-3K Plain Weave | 3K | Tissu uni | 160 | 0.18 | 0-2.3 |
ZC-3KTwill Weave | 3K | Tissu sergé | 160 | 0.18 | 0-2.3 |
ZC-3K Plain Weave | 3K | Tissu uni | 200 | 0.22 | 0-2.3 |
ZC-3K Twill Weave | 3K | Tissu sergé | 200 | 0.22 | 0-2.3 |
ZC-3K Plain Weave | 3K | Tissu uni | 280 | 0.3 | 0-2.3 |
ZC-3K Twill Weave | 3K | Tissu sergé | 280 | 0.3 | 0-2.3 |
ZC-12K Plain Weave | 12K | Tissu uni | 400 | 0.45 | 0-2.3 |
ZC-12K Twill Weave | 12K | Tissu sergé | 400 | 0.45 | 0-2.3 |
ZC-12K Plain Weave | 12K | Tissu uni | 450 | 0.5 | 0-2.3 |
ZC-12KTwill Weave | 12K | Tissu sergé | 450 | 0.5 | 0-2.3 |
Type | Style | Tissage | Poids (g/m²) | Épaisseur (mm) | Largeur (m) |
---|---|---|---|---|---|
ZC-200D-60P | 200d | Tissu uni | 60 | 0.08 | 0-2.3 |
ZC-400D-100P | 400d | Tissu uni | 100 | 0.12 | 0-2.3 |
ZC-400D-120P | 400d | Tissu uni | 120 | 0.14 | 0-2.3 |
ZC-400D-140P | 400d | Tissu uni | 140 | 0.16 | 0-2.3 |
ZC-1100D-170P | 1100d | Tissu uni | 190 | 0.2 | 0-2.3 |
ZC-1100D-200P | 1100d | Tissu uni | 200 | 0.22 | 0-2.3 |
ZC-1100D-220P | 1100d | Tissu uni | 220 | 0.24 | 0-2.3 |
ZC-1100D-270P | 1100d | Tissu uni | 270 | 0.3 | 0-2.3 |
ZC-1680D-320P | 1680d | Tissu uni | 320 | 0.34 | 0-2.3 |
ZC-1680D-335P | 1680d | Tissu uni | 335 | 0.35 | 0-2.3 |
ZC-1680D-410P | 1680d | Tissu uni | 410 | 0.45 | 0-2.3 |
ZC-3300D-420P | 3300d | Tissu uni | 420 | 0.5 | 0-2.3 |
Stylet | Résistance à la traction | Module d'élasticité | Allongement à la rupture | Poids (g/m²) |
---|---|---|---|---|
T300-12000 | ≥3500Mpa | ≥230Gpa | ≥1.5% | 198 |
T300-12000 | ≥3500Mpa | ≥230Gpa | ≥1.5% | 396 |
T700S-12000 | ≥4900Mpa | ≥240Gpa | ≥2.1% | 400 |
T700S-12000 | ≥4900Mpa | ≥240Gpa | ≥2.1% | 800 |
T800S-12000 | ≥5800Mpa | ≥294Gpa | ≥2.0% | 515 |
T800S-12000 | ≥5800Mpa | ≥294Gpa | ≥2.0% | 1030 |
Style | Tissage | Poids (g/m²) | Épaisseur (mm) | Largeur (m) |
---|---|---|---|---|
3K、1000d | Tissu uni | 155 | 0.26 | 0-2.3 |
3K、1000d | Tissu sergé | 165 | 0.28 | 0-2.3 |
3K、1000d | Tissu uni | 185 | 0.3 | 0-2.3 |
3K、1000d | Tissu sergé | 185 | 0.3 | 0-2.3 |
3K、1500d | Tissu uni | 60 | 0.2 | 0-2.3 |
3K、1500d | Tissu sergé | 220 | 0.24 | 0-2.3 |
3K、1500d | Tissu uni | 190 | 0.28 | 0-2.3 |
3K、1500d | Tissu sergé | 190 | 0.28 | 0-2.3 |
Type | Style | Structure | Direction axiale | Poids (g/m²) | Largeur (mm) |
---|---|---|---|---|---|
ZC-D1 | 12K | Biaxe | 0°90° | 150-400 | 1270 |
ZC-D2 | 12K | Biaxe | ±45° | 150-400 | 1270 |
ZC-D3 | 12K | Biaxe | 0°45° | 150-400 | 1270 |
ZC-D4 | 12K | Biaxe | 45°90° | 150-400 | 1270 |
ZC-T1 | 12K | Triaxial | ±45°90° | 225-600 | 1270 |
ZC-T2 | 12K | Triaxial | 0°±45° | 225-600 | 1270 |
ZC-T3 | 12K | Triaxial | 0°90°45° | 225-600 | 1270 |
ZC-T4 | 12K | Triaxial | 0°90°-45° | 225-600 | 1270 |
ZC-Q1 | 12K | Quadraxe | ±45°0°90° | 300-800 | 1270 |